PAU TAI INDUSTRIAL (THAILAND) COMPANY LTD was established on May 2004. We received approval from Board of Investment in Thailand and acquired the assets of OMG (Thailand) Company Limited in November 2004 with the intention of expanding our Company. After manufacturing site had been renovated and upgraded, PAU TAI INDUSTRIAL (THAILAND) COMPANY LTD has started the production of PVC Stabilizers in January 2005. We increased the range of our products by introducing Paint Driers, polyester Promoters, Catalyst in the following year. Today, PAU TAI INDUSTRIAL (THAILND) COMPANY LTD provide its versatility by expanding the range of its products which are the broad spectrum of liquid Ba/Cd/Zn, Ba/Zn and Ca/Zn PVC Stabilizers, Paint Driers, Polyester Promoters, Wood Preservatives/Fungicides, Catalyst as well as Lubricant additives in order to satisfy variety of consumer and business. We are committed to provide the technical innovation by delivering better, safer, wider product portfolios in order to continually achieve our customer satisfaction with high quality products and excellent services. Our plant has the capacity to manufacture about 3600 tons per annum of the above products with the flexibility to manufacture customized grades tailored to customer specifications. Our products are well accepted by all Multinational and Local manufacturers of Paint, Varnishes, Polyester Resins in Thailand. We are regularly exports our UNINOX grade Paint Driers, Polyester Promoters, PVC Stabilizers to South East Asia and Middle East. Our Quality Control Laboratory is well equipped with modern instruments and well trained technical personnel to deliver the “BEST QUALITY” to our valued customer for long term business relationships. Following properties will be tested for each lot delivered to our customers as a commitment for better service with competitive price based on our Innovative Technology on Metal Carboxylates.

• % Metal • Color • Non Volatile Matter (% Solids) • Acid Value • % Moisture • Viscosity • Density • Flash point

Our R&D Department strives continuously to further improve the products “Quality” by applying in our Innovative Technology on Metal Carboxylates. UNINOX grade driers are based on 2 Ethyl hexanoic acid. They are formulated to impart high metal contents and low viscosity. Neodecanoate/Versates and Naphthenate based Paint Driers are also available.
UNINOX driers are offered as highly balanced liquid systems characterized by (1) Purity of highest order. (2) Good Stability and Solubility in various vehicles. (3) Retention of clarity over long periods of time. (4) Low Viscosity for easier handling. (5) Certified metal content. (6) High metal content with no tendency to crystallize or sludge out. (7) Resistance to atmospheric and climatic conditions. (8) Resistance to colloidal shock. (9) Less tendency to be absorbed. (10) Odourless. Cobalt Octoate is the most active surface drier. Cobalt effects rapid surface drying and is generally used in conjunction with auxiliary driers. It is usually added at 0.05 to 0.4 % based on vehicle solids. It is a strong oxidant. It is compatible with all surfaces coating media. Atmospheric humidity does not affect Cobalt drier. This unique feature prevents water vapor present in atmosphere from penetrating the paint film.
Cobalt Octoate being the most effective drier promotes polymerization of media, hardens the paint film, improves gloss and water resistance and reduces brittleness of film. The careful use of Cobalt octoate gives the paint film a good gloss, free from frosting tendency. This drier is a universal drier, which is essential in all the media and is capable of performing individually giving reasonable properties to the paint film.
In air-drying type insulating varnishes use of Cobalt Octoate increases water resistance, but the excessive use of Cobalt octoate causes brittleness and early failure of insulation.
Cobalt Octoate accelerates the catalytic action of Methyl Ethyl Ketoxime (MEKO) to polymerize unsaturated polyester resin. The typical characteristics of certain concentrations of UNINOX grade Cobalt Octoate are as under:

Product Name	Cobalt, % (w/w)	Colour	Physical State	Density at 30 °C, gm/ml	Non volatile matter, % w/w	Viscosity at 30°C, cSt
UNINOX Co 12	12 ± 0.2	Blue	Liquid	1.02 ± 0.04	65 ± 5	200 max
UNINOX Co 10	10 ± 0.2	Blue	Liquid	0.98 ± 0.04	55 ± 5	100 max
UNINOX Co 08	8 ± 0.2	Blue	Liquid	0.90 ± 0.04	41 ± 5	50 max
UNINOX Co 06	6 ± 0.2	Blue	Liquid	0.88 ± 0.04	32 ± 5	50 max

Manganese Octoate is a very stable auxiliary drier. It is an active drier metal and strong oxidant, promotes polymerization to a greater degree than cobalt. It is often used alone in backing finishes and in combination with Lead and Cobalt in air-dry applications.
Manganese Octoate is mainly used in exterior paints, floor finishes, backing enamels and in the paints where colour is not a constraint. The dosage of Cobalt octoate can be minimized by using Manganese Octoate as it is capable of replacing Cobalt because of its high activity.
Manganese Octoate prevents paint film from the wrinkling effect. Manganese Octoate is not recommended in white finishes as it gives a typical tinting effect of its own colour. The typical characteristics of certain concentrations of our UNINOX grade Manganese Octoate are as under:

Product Name	Cobalt, % (w/w)	Colour	Physical State	Density at 30 °C, gm/ml	Non volatile matter, % w/w	Viscosity at 30°C, cSt
UNINOX Mn 10	10 ± 0.2	Dark brown	Liquid	0.98 ± 0.05	55 ± 7	300 max
UNINOX Mn 06	6 ± 0.2	Dark brown	Liquid	0.90 ± 0.05	30 ± 7	100 max